BELANA , J.

In the present work, a XLPE mid-voltage cable from General Cable CO. has been studied by Thermally stimulated depolarization currents. Systematic measurements have been carried out in order to compare the conductive processes in this cable with previous results. Depolarization current as a function of thermal annealing, thermal history,...

It is well established that space charge conditions insulation lifetime. Because of this, space charge formation and relaxation processes characterization has become a very active research field, not only from an basic science point of view, but also in order to improve insulation performance in cable and other devices. In the case of...

Conductivity () in XLPE insulation of power cables annealed at 90 ºC at temperatures between 50 and 97 ºC has been measured. In all cases there is an initial increase in conductivity that develops a maximum and finally decreases for long annealing times. This maximum appears in the sample annealed 20 days when conductivity is measured at 50 ºC...

A new study of the electrical conductivity of crosslinked polyethylene (XLPE) mid-voltage (MV) cable insulation is presented. Its main objective is to show the effect of annealing treatments on MV cables under actual service conditions. Complementary time domain (absorption/resorption currents) and frequency domain (dynamic electrical analysis)...