AgDLC coatings were deposited by magnetron sputtering in order to evaluate: i) the Ag nanoparticle size distribution along the coatings thickness and ii) the silver stability in DLC coatings. Four different coatings were deposited, two AgDLC nanocomposite coatings containing 20 at.% of Ag, with thicknesses of 250 nm and 1000 nm, a 250 nm AgDLC...

Zirconium carbonitride coatings with silver nanoparticles were produced by DC unbalanced dual magnetron sputtering system, using two targets, Zr and Zr/Ag in an Ar, C2H2 and N2 atmosphere. Stainless steel 316L and silicon (100) substrates were used for electrochemical and structural characterization, respectively. Silver was found to be well...

New multifunctional materials based on well-established materials to which functional properties are added, such as antibacterial performance, have become a relevant research topic, in order to meet the requirements of today's technological advances. This paper reports the results of a detailed structural and chemical characterization study of...

This paper is focused on the sputtering process and on the structure, chemical composition and mechanical properties of coatings consisting of Al\O dielectric matrix incorporated with increasing Au contents. The maximum Au content incorporated in the coatings was 9 at.%. Al was in deficient values in relation to the Al2O3 compound. Al\O matrix...

In the present study, nanocomposite coatings of Au clusters embedded in two different oxides, TiO2 and Al2O3, were synthesized using pulsed DC magnetron sputtering. The depositions were carried out in three steps, by depositing the oxide, the Au clusters, and again the oxide. The deposition time of the Au clusters was varied in order to achieve...

Ag–TiCN coatings were deposited by dc reactive magnetron sputtering and their structural and morphological properties were evaluated. Compositional analysis showed the existence of Ag–TiCN coatings with different Ag/Ti atomic ratios (ranging from 0 to 1.49). The structural and morphological properties are well correlated with the evolution of...

Ti–Si–C–ON films were deposited by DC reactive magnetron sputtering using different partial pressure of oxygen (pO2) and nitrogen (pN2) ratio. Compositional analysis revealed the existence of two different growth zones for the films; one zone deposited under low pO2/pN2 and another zone deposited under high pO2/pN2. The films produced under low...