DI GIOIA , G.

AbstractQuasi-vertical gallium nitride (GaN) Schottky diodes on silicon carbide (SiC) substrates were fabricated for frequency multiplier applications. The epitaxial structure employed had an n− layer of 590 nm with doping 6.6 × 1016 cm−3, while the n+ layer was 950 nm thick, with doping 2 × 1019 cm−3. Potassium hydroxide (KOH) chemical surface...

A model to predict the ideal reverse leakage currents in Schottky barrier diodes, namely, thermionic emission and tunneling components, has been developed and tested by means of current–voltage–temperature measurements in GaN-on-SiC devices. The model addresses both current components and both forward and reverse polarities in a unified way and...