FERENC , J.

Temperature dependence of magnetic properties of nanocrystalline Fe60Co18Cu1B15Nb6−xZrx (x =0, 3, 6) alloys has been studied at different stages of devitrification. Transmission electron microscopy shows nanocrystals of the size �5 nm, which remains almost constant along the nanocrystallization process. Curie temperature of the residual...

Hysteresis loops of nanocrystalline samples of Fe39Co39Nb6B16 - yCuy (y = 0, 1) HITPERM-type alloys were measured from room temperature up to 773K. The alloy with Cu shows a nearly constant value of coercivity (∼ 135A/m) in all the studied temperature range, whereas for the Cu-free alloy, the coercivity increases from 125A/m at 300K up to...

Temperature evolution of the coercivity of nanocrystalline samples of Fe60Co18Nb6B15Cu1 alloy with different crystalline fractions was measured from room temperature up to 690 K. Although room temperature coercivity increases as the nanocrystallization progresses, the thermal stability of the magnetic properties of the system is clearly...