The fuel outgassing efficiency from plasma-facing components exposed in JET-ILW has been studied at ITER-relevant baking temperatures. Samples retrieved from the W divertor and Be main chamber were annealed at 350 and 240 °C, respectively. Annealing was performed with thermal desoprtion spectrometry (TDS) for 0, 5 and 15 h to study the...
-
August 25, 2020 (v1)PublicationUploaded on: December 4, 2022
-
August 27, 2020 (v1)Publication
Rotating collectors and quartz microbalances (QMBs) are used in JET to provide time-dependent measurements of erosion and deposition. Rotation of collector discs behind apertures allows recording of the long term evolution of deposition. QMBs measure mass change via the frequency deviations of vibrating quartz crystals. These diagnostics are...
Uploaded on: December 4, 2022 -
July 3, 2020 (v1)Publication
Effect of ELMs on fuel retention at the bulk W target of JET ITER-Like Wall was studied with multi-scale calculations. Plasma input parameters were taken from ELMy H-mode plasma experiment. The energetic intra-ELM fuel particles get implanted and create near-surface defects up to depths of few tens of nm, which act as the main fuel trapping...
Uploaded on: December 4, 2022 -
July 3, 2020 (v1)Publication
Selected set of samples from JET ITER-Like Wall (JET-ILW) divertor tiles exposed in 2015–2016 has been analysed using Thermal Desorption Spectrometry (TDS). The deuterium (D) amounts obtained with TDS were compared with Nuclear Reaction Analysis (NRA). The highest amount of D was found on the top part of inner divertor which has regions with...
Uploaded on: March 25, 2023 -
July 1, 2020 (v1)Publication
Selected set of samples from JET TER-Like Wall (JET-ILW) divertor tiles exposed both in 20132014 and 20112014 has been analysed using Thermal Desorption Spectrometry (TDS). The deuterium (D) amounts ob tained with TIS were compared with ion Beam Analysis (TBA) and Secondary ion Mass Spectrometry (SIMS) data. The hig amount of D was found on the...
Uploaded on: March 25, 2023