Tritium (T) distributions on tungsten (W)-coated plasma-facing tiles used in the third ITER-like wall campaign (2015-2016) of the Joint European Torus (JET) were examined by means of an imaging plate technique and beta-ray induced x-ray spectrometry, and they were compared with the distributions after the second (2013-2014) campaign. Strong...
-
July 8, 2020 (v1)PublicationUploaded on: December 4, 2022
-
July 14, 2020 (v1)Publication
The first divertor was installed in the JET machine between 1992 and 1994 and was operated with carbon tiles and then beryllium tiles in 1994-5. Post-mortem studies after these first experiments demonstrated that most of the impurities deposited in the divertor originate in the main chamber, and that asymmetric deposition patterns generally...
Uploaded on: December 5, 2022 -
August 25, 2020 (v1)Publication
The fuel outgassing efficiency from plasma-facing components exposed in JET-ILW has been studied at ITER-relevant baking temperatures. Samples retrieved from the W divertor and Be main chamber were annealed at 350 and 240 °C, respectively. Annealing was performed with thermal desoprtion spectrometry (TDS) for 0, 5 and 15 h to study the...
Uploaded on: December 4, 2022 -
August 25, 2020 (v1)Publication
Tungsten-coated divertor tiles exposed during the third JET ITER-Like Wall (ILW) campaign in 2015–2016 (ILW3) were studied with Secondary Ion Mass Spectrometry (SIMS). ILW-3 campaign contained more high-power plasma discharges and longer plasma time than the earlier ILW campaigns. Measurements showed increased beryllium (Be) deposition on the...
Uploaded on: March 27, 2023 -
July 3, 2020 (v1)Publication
Selected set of samples from JET ITER-Like Wall (JET-ILW) divertor tiles exposed in 2015–2016 has been analysed using Thermal Desorption Spectrometry (TDS). The deuterium (D) amounts obtained with TDS were compared with Nuclear Reaction Analysis (NRA). The highest amount of D was found on the top part of inner divertor which has regions with...
Uploaded on: March 25, 2023 -
July 1, 2020 (v1)Publication
Selected set of samples from JET TER-Like Wall (JET-ILW) divertor tiles exposed both in 20132014 and 20112014 has been analysed using Thermal Desorption Spectrometry (TDS). The deuterium (D) amounts ob tained with TIS were compared with ion Beam Analysis (TBA) and Secondary ion Mass Spectrometry (SIMS) data. The hig amount of D was found on the...
Uploaded on: March 25, 2023