SMIRNOV , B. I.

The microstructural characteristics and amplitude dependences of the Young's modulus E and internal friction (logarithmic decrement delta) of biocarbon matrices prepared by beech wood carbonization at temperatures T (carb) = 850-1600A degrees C in the presence of a nickel-containing catalyst have been studied. Using X-ray diffraction and...

The thermal conductivity k and resistivity ρ of biocarbon matrices, prepared by carbonizing medium-density fiberboard at Tcarb = 850 and 1500°C in the presence of a Ni-based catalyst (samples MDFC( Ni)) and without a catalyst (samples MDF-C), have been measured for the first time in the temperature range of 5–300 K. X-ray diffraction analysis...

С использованием прецизионной интерферометрической методики измерены деформационные характеристики и прочность при одноосном сжатии биоуглеродного материала на основе бука, частично графитизированного в результате применения Ni-содержащего катализатора в процессе карбонизации при различных температурах. Показано, что при комнатной температуре...