The amorphous alloys Gd60Co40−xMnx (x = 0, 5, 10, 15) were prepared by melt spinning. The Curie temperature,T c, increases monotonously with Mn addition, ranging from 198 K for x = 0 to 205 K for x = 15, while the maximum values of −ΔSM under the applied field change from 0 to 5 T are 7.7, 7.1, 6.2 and 5.4 J·kg−1·K−1 for x = 0, 5, 10, and 15,...

The structure and magnetic properties of polycrystalline GdCo9Si2 compound have been investigated. It has a BaCd11 structure and undergoes two magnetic phase transitions: an antiferromagnetic to ferrimagnetic transition occurring at rv93 K, and a ferrimagnetic to paramagnetic transition at 420 K, which results in a positive and a negative...

Gd5Si2.05-xGe1.95-xNi2x (2x ¼ 0.08, 0.1) alloys were prepared by arc melting followed by annealing at 1273 K for 96 h. Mixed monoclinic Gd5Si2Ge2-type phase, orthorhombic Gd5Si4-type phase, and a small amount of Gd5Si3-type phase were obtained in these alloys. Gd5Si2.01Ge1.91Ni0.08 alloy undergoes a second-order transition (TC) around 300 K,...