Amorphous Phase Formation and Heat Treating Evolution in Mechanically Alloyed Ti–Cu Alloy for Biomedical Applications

Description

This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Abstract

The present work aims to produce TixCu100-x (x=90, 80, 70, and 60) amorphous alloys by using high energy ball mill. The microstructure and possible formation of amorphous phases were characterized employing laser granulometry, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray difraction (XRD). The amorphous-crystalline transformation at high temperatures was studied according to diferential scanning calorimetry (DSC) and XRD. The Ti80Cu20 alloys were obtained in an amorphous state after 30 h of mechanical alloying, and the amorphous phase is stable up to 340 °C. At higher temperatures, this alloy crystallizes, forming the intermetallic compound Ti2Cu, and a substitutional solid solution Ti(Cu).

Additional details