The magnetocaloric effect of partially crystalline Fe-B-Cr-Gd alloys.

Description

The influence of annealing temperature and crystallization on the magnetocaloric effect (MCE) of Fe-B-Cr-Gd partially crystalline alloys was studied. Although the alloys exhibited dissimilar devitrification behavior, all the alloys exhibited MCE behavior consistent with a phenomenological universal curve and theoretical power law expressions of the magnetic field dependence of MCE. The TC of partially crystalline Fe75B12Cr8Gd5alloys increased with increasing annealing temperatures. However, peak magnetic entropy change and refrigerant capacity values remained relatively constant, suggesting that these alloys are promising for active magnetic regenerator applications.