Unravelling the optimization of few-layer graphene crystallinity and electrical conductivity in ceramic composites by Raman spectroscopy

Description

Zirconia composites with few-layer graphene (FLG) were prepared by two powder processing routines -ultrasonic agitation or planetary ball milling- and spark plasma sintered at 1250 and 1300 °C. An in-depth study of the crystallinity of FLG, in terms of presence and nature of defects, was performed by Raman spectroscopy, revealing enhanced FLG crystallinity after sintering. This enhancement was more noticeable in the composites sintered at the highest temperature, with lower amount of structural defects and amorphous carbon. However, remaining amorphous carbon was detected in the composites prepared by planetary ball milling even after sintering at the highest temperature, resulting in lower electrical conductivities. Optimum results in terms of electrical conductivity were achieved for the composites prepared by ultrasonic agitation and sintered at 1300 °C, with electrical percolation limit below 2.5 vol% FLG and high electrical conductivity (678 S/m for 5 vol% FLG), as result of the enhanced FLG crystallinity after sintering.

Abstract

Ministerio de Ciencia, Innovación y Universidades PGC 2018- 101377-B-100

Abstract

Ministerio de Asuntos Económicos y Transformación Digital BES-2016- 078711

Abstract

Universidad de Sevilla USE-18740-H

Additional details