1999 (v1)
Publication
No description
Uploaded on: April 14, 2023
F
R
FERRO , Riccardo
Last name: FERRO
First name: Riccardo
Institution: UNIGE
Links
-
-
2000 (v1)Publication
No description
Uploaded on: April 14, 2023 -
1999 (v1)Publication
No description
Uploaded on: March 31, 2023 -
2000 (v1)Publication
No description
Uploaded on: April 14, 2023 -
2000 (v1)Publication
No description
Uploaded on: March 31, 2023 -
1999 (v1)Publication
No description
Uploaded on: March 31, 2023 -
2008 (v1)Publication
This book emphasizes the chemical aspects of the intermetallic science and therefore the mutual reactivity of metals and the characteristics of intermetallic compounds. Topics included are: Phase diagrams of alloy systems; Selected aspects of intermetallics structural chemistry with emphasis on the solid state; Intermetallic reactivity trends...
Uploaded on: March 31, 2023 -
2001 (v1)Publication
No description
Uploaded on: March 25, 2023 -
2002 (v1)Publication
No description
Uploaded on: March 25, 2023 -
1998 (v1)Publication
No description
Uploaded on: March 31, 2023 -
1995 (v1)Publication
No description
Uploaded on: March 27, 2023 -
1995 (v1)Publication
No description
Uploaded on: April 14, 2023 -
1984 (v1)Publication
The data in the literature relevant to the phase diagrams of the RIn systems (R ≡ rare earth) are analysed, and recent measurements of the melting temperatures of a few selected alloys of the RIn systems are reported. Experimental data from various laboratories are also compared and discussed in connection with the general methodologies applied...
Uploaded on: April 14, 2023 -
1990 (v1)Publication
On the basis of the similarities in the alloying behaviours of the different rare earths, the constitutional properties of a few selected promethium alloys are here estimated. Phase diagrams, crystal structures (and lattice parameters) are proposed for the binary alloys of Pm with Mn, Fe, Cu, Ag, Au, Ga, In and Tl. © 1990.
Uploaded on: April 14, 2023 -
1999 (v1)Publication
No description
Uploaded on: December 2, 2022 -
1981 (v1)Publication
The Pr-Tl system was studied in the composition range 15-100 at.% Tl using differential thermal analysis, metallography and X-ray examination. The praseodymium-rich alloys were reinvestigated and the published phase diagram was confirmed. The following intermetallic compounds were observed: Pr3Tl (decomposes at 800 ± 10 °C); Pr2Tl (decomposes...
Uploaded on: April 14, 2023 -
1991 (v1)Publication
No description
Uploaded on: March 31, 2023 -
1988 (v1)Publication
The data in the literature relevant to the intermediate phases and to the state diagrams of the R-Tl systems (R ≡ rare earth) are analysed and discussed in connection with the methodologies applied to the study of the alloy constitution. On the basis of the various data available, a number of values for the characteristic constants of the...
Uploaded on: April 14, 2023 -
1990 (v1)Publication
No description
Uploaded on: April 14, 2023 -
1990 (v1)Publication
The Nd-Mg system was studied using differential thermal analysis (DTA), X-ray examination, metallography, and microprobe analysis. The following intermetallic compounds were found to exist and their crystal structures confirmed or determined: NdMg (cubic, cP2 CsCl type, melting point 800 °C), NdMg2 (cubic, cF24 MgCu2 type, peritectic formation...
Uploaded on: April 14, 2023 -
1985 (v1)Publication
The general properties of rare earth-manganese alloys are described and reviewed. The Pr-Mn system was studied using differential thermal analysis, X-ray examination, metallography and microprobe analysis. Both the stable phase diagram and information on the metastable equilibria were obtained. Evidence of the peritectic formation (790 °C) of...
Uploaded on: April 14, 2023 -
1995 (v1)Publication
No description
Uploaded on: April 14, 2023 -
1982 (v1)Publication
The Sm-In system was studied using differential thermal, metallographic and X-ray analyses. The following intermediate phases were observed: Sm2In (melting point, 1090 ± 10 °C), Sm1+xIn (melting point, 1210 ± 20 °C), Sm3In5 (melting point, 1110 ± 10 °C) and SmIn3 (melting point, 1130 ± 10 °C). Five eutectics occur: β-Sm2In (905 ± 5 °C, 16.5 ± 1...
Uploaded on: April 14, 2023 -
1979 (v1)Publication
The Pr-In system has been studied in the composition range 30-100 at.% In by differential thermal analysis, metallography and X-ray examination. The Pr-rich alloys have been reinvestigated and confirmed. The following intermediate phases were observed: Pr3In (decomposes at 930 ± 10 °C), Pr2In (decomposes at 1020 ± 10 °C), Pr1+xIn (m.p. 1170 ±...
Uploaded on: April 14, 2023