The magnetic entropy change (ΔSM), temperature of peak ΔSM (Tpk) and refrigerant capacity (RC) in Fe(RE)80B12Cr8 (RE = La, Ce, or Gd) alloys were studied. Increasing La, Ce, and Gd content led to relatively constant, decrease, and increase in Tpk, respectively. Both the phenomenologically constructed universal curve for ΔSM and field dependence...

A procedure has been developed to directly measure the adiabatic temperature change of amorphous melt-spun Fe-based ribbons displaying attractive room temperature magnetocaloric properties. Polycrystalline Gd ribbons are used as a reference material to compensate for the contribution of the sample holder to the experimental values. Fe78B12Cr8Ce...

The influence of annealing temperature and crystallization on the magnetocaloric effect (MCE) of Fe-B-Cr-Gd partially crystalline alloys was studied. Although the alloys exhibited dissimilar devitrification behavior, all the alloys exhibited MCE behavior consistent with a phenomenological universal curve and theoretical power law expressions of...

Gd5Si2.05-xGe1.95-xNi2x (2x ¼ 0.08, 0.1) alloys were prepared by arc melting followed by annealing at 1273 K for 96 h. Mixed monoclinic Gd5Si2Ge2-type phase, orthorhombic Gd5Si4-type phase, and a small amount of Gd5Si3-type phase were obtained in these alloys. Gd5Si2.01Ge1.91Ni0.08 alloy undergoes a second-order transition (TC) around 300 K,...